Alloy 20

 Home / Alloy 20

ASTM B473 Alloy 20 Bars - ASTM B473 Alloy 20 Bars DIN/EN/ASTM/ASME, extensive range of ASTM B473 Alloy 20 Bars


Silver Tubes manufacturer, fabricator & suppliers of ASTM B473 Alloy 20 Bars, Forged Fittings, Threaded Pipe Fittings, premier supplier of bulk ASTM B473 Alloy 20 Bars stock worldwide


Fast delivery guaranteed for every size and class ASTM B473 Alloy 20 Bars, Socket Weld Fittings & Forged Flanges, largest range of ASTM B473 Alloy 20 Bars Supplies in India


Alloy 20 is one of the so-called "Super" stainless steels that was designed for maximum resistance to acid attack. It's nickel, chromium, molybdenum and copper content contribute to its overall resistance to chlorideon stress corrosion cracking and general pitting attack. The alloy is stabilized with columbium to minimize carbide precipitation during welding. It has good mechanical properties and can be fabricated with comparative ease. Athough the alloy was designed for use in sulfuric acid related industries, it finds wide usage throughout the chemical processing industry. It also is used for processing pharmaceuticals, food, gasoline, solvents, plastics, explosives, synthetic fibers and many other products.



Specifications


Standard Alloy 20
UNS N08020
Werkstoff Nr. 2.4660

Chemical Composition


Alloy 20
Ni 32 – 38
Fe Bal
Cr 19 – 21
Cu 3 – 4
Mo 2 – 3
Nb 0.1 – 0.3
C 0.02 max
Mn 1 – 2
P 0.02 max
S 0.005 max
Si 0.7 max

Mechanical & Physical Properties – Alloy 20


Density 8.1 g/cm3
Melting Point 1443 °C (2430 °F)
Tensile Strength Psi – 80000 , MPa – 551
Yield Strength (0.2%Offset) Psi – 35000 , MPa – 241
Elongation 30 %

SPECIFICATIONS
ASTM B729, ASTM B464, ASTM B366, ASTM B473, ASTM B462
ASME SB729, ASME SB464, ASME SB366, ASME SB473, ASME SB462

TENSILE REQUIREMENTS

Tensile Strength (KSI) 80
Yield Strength (KSI) 35KSI can be converted to MPA (Megapascals) by multiplying by 6.895